POLY EMULATION

Emulsion matte paint with a high quality external use consisting of acrylic copolymer and other chemicals to gain durability and resistance to weather and gives excellent properties for the application, and in conformity with the standards and specifications Arabia No. 2002/470.

APPLICATION

This is recommended as a class final for walls and ceilings, panels, gypsum and concrete surfaces for external use.

Density 1.5 at a temperature ° 25 m.

.ASTM D-14

Viscosity 105 Unit Corps at a temperature

° 25 m. .ASTM D-562

Solid content 40% by volume .ASTM D-5201
Coverage rate 3 m ² / Kg, at a dry layer thickness of 40 microns without dilution.
Water resistance Passing 7 days, .ASTM D-870
Alkali resistance Passing        7        days)                       solution concentration%1ASTM D-1308
Resistance salts Passing        7        days)                       solution concentration% 1.5 (. .ASTM D-

1308

Dryness time Surface dry 30 minutes.

Two hours to complete dryness.

Time interval between two     layers coating Minimum 4 hours.
Diluted water
Dilution ratio 10-15% (by volume, when using a roller and brush.

And it depends on the weather conditions when in use

Adhesion strength pass, .ASTM D-3359
  • Application Instructions
    • Surface preparation and the preparation of a good clean it
    • Remove the old paint (if any) completely out of the surface, and to make sure that the surface completely clean and free of dirt, dust, oils and
    • A single layer of the base coating and leave it to dry .
    • Two Coat recommended from Emulsion.

     

    Application tools:

    Roller Brush: Basic.

Package

Pail 20 kg &1 Gallon

Validity of the product storage

Almost 12 months in a closed container – suitable cool, dry and ventilated place.

Special Instructions

  • You must paint mixing well until it becomes homogeneous before
  • Dilution appropriate quantity using a water to get the proper
  • Do not paint over wet surfaces only after fully dry drier.
  • Not apply the next layer coating unless the previous layer to dry
  • Desired temperature 25-40 ° C, at
  • Surface must be free of moisture and not less than 8% and moisture content of not more than 70%.